Oxygen sensing behaviors of Eu (Ba1-xPrx)2Cu3O7-δ and Eu1-yPrBa2Cu3O7-δ ceramic rods with hot-spot / Ikhwan Adzam

Oxygen sensing properties of Pr doped EuBa2Cu307-c5 short ceramic rods were investigated. The Eu(Bai-xPrx)zCu307-o (x=O, 0.05, 0.25 and x=0.40) and EuiyPryBa2Cu307- a (y=O, 0.05, 0.1 0, 0.15 and y=0.20) rods with dimensions of around 13mm x 0.65mm x 0.65mm and 13mm x 1.48mm x 1.48mm, respectively we...

Full description

Saved in:

Bibliographic Details
Main Author:	Adzam, Mohd Ikhwan
Format:	Thesis
Language:	English
Published:	2015
Subjects:	TP Chemical technology Chemical engineering
Online Access:	https://ir.uitm.edu.my/id/eprint/14044/1/TM_MOHD%20IKHWAN%20ADZAM%20AS%2015_5.pdf
Tags:	Add Tag No Tags, Be the first to tag this record!

id	my-uitm-ir.14044
record_format	uketd_dc
spelling	my-uitm-ir.140442022-04-18T04:28:28Z Oxygen sensing behaviors of Eu (Ba1-xPrx)2Cu3O7-δ and Eu1-yPrBa2Cu3O7-δ ceramic rods with hot-spot / Ikhwan Adzam 2015-04 Adzam, Mohd Ikhwan TP Chemical technology Chemical engineering Oxygen sensing properties of Pr doped EuBa2Cu307-c5 short ceramic rods were investigated. The Eu(Bai-xPrx)zCu307-o (x=O, 0.05, 0.25 and x=0.40) and EuiyPryBa2Cu307- a (y=O, 0.05, 0.1 0, 0.15 and y=0.20) rods with dimensions of around 13mm x 0.65mm x 0.65mm and 13mm x 1.48mm x 1.48mm, respectively were prepared by standard solid state reaction method. For the first series of this study, Eu(Ba1-xPrxhCu307_0 rods were prepared to investigate the influences of changes in structure and the expected decrease in average Cu valence on oxygen sensing properties. X-ray powder diffraction analysis showed that orthorhombicity of the structure reduces with increasing Pr concentration. After the hot-spot became visible, samples x=O and x=0.05 showed a sudden drop in current before remaining constant with increasing voltage. This is suggested to be due to steep increase in resistivity caused by the sudden increase in temperature of the hot-spot together with the structural changes that lead to reduction in oxygen content. However, for the x=0.25 and x=0.4 rods the output current shows no sudden drop. The results also showed that the reduced magnitude of the output current with increasing Pr could be attributed to the reduction in intrinsic hole concentration. The output current for all samples showed strong dependence on p02. Although the sensitivity of the output current to p02 between 50% p02 and 100% p02 reduces with increasing x, the stability and repeatability of the output current seems to improve. Also, while Pr doped Eu(BaixPrx) 2Cu307_0 reduces the magnitude of the output current, it produces better response time towards different p02. On the other hand, Eui-yPryBazCu307-a rods were prepared and X-Ray powder diffraction analysis showed that, Pr doped Eu1-yPryBazCu307-o were all orthorhombic in unit cell structure with reduction in orthorhombicity upon doping. The /-V curve showed a relatively constant output current after the appearance of hot-spot. Meanwhile, the magnitude of the constant output current was observed to be decreasing with increasing Pr doping which indicates possible reduction in intrinsic hole concentration. In addition, the output current for rods with y=O.O, 0.05 and 0.10 showed a sudden drop upon the appearance of hot-spot, due to the sudden increase in hot-spot temperature, before becoming slightly constant. However, the sudden drop of output current upon appearance of hot-spot was not observed when Pr was increased to y=0.15 and 0.20 but instead a stable output current was observed. Interestingly, the output current after appearance of hot-spot for all rods showed strong dependency on ambient oxygen concentration. The sensitivity for each rod however, reduces with increasing ambient oxygen concentration. Pr doped Eui-yPryBazCu307_0 seems to prevent the sensitivity from dropping to almost zero as was the case of Eu(Ba1_ yPry)2Cu30 7_0 rods due to existence of Cu-0 chains in the orthorhombic structure. Pr doping (for y=O.lO) has also resulted in better oxygen absorption response time and better output current stability compared to other rods. 2015-04 Thesis https://ir.uitm.edu.my/id/eprint/14044/ https://ir.uitm.edu.my/id/eprint/14044/1/TM_MOHD%20IKHWAN%20ADZAM%20AS%2015_5.pdf text en public mphil masters Universiti Teknologi MARA Faculty of Applied Sciences
institution	Universiti Teknologi MARA
collection	UiTM Institutional Repository
language	English
topic	TP Chemical technology Chemical engineering
spellingShingle	TP Chemical technology Chemical engineering Adzam, Mohd Ikhwan Oxygen sensing behaviors of Eu (Ba1-xPrx)2Cu3O7-δ and Eu1-yPrBa2Cu3O7-δ ceramic rods with hot-spot / Ikhwan Adzam
description	Oxygen sensing properties of Pr doped EuBa2Cu307-c5 short ceramic rods were investigated. The Eu(Bai-xPrx)zCu307-o (x=O, 0.05, 0.25 and x=0.40) and EuiyPryBa2Cu307- a (y=O, 0.05, 0.1 0, 0.15 and y=0.20) rods with dimensions of around 13mm x 0.65mm x 0.65mm and 13mm x 1.48mm x 1.48mm, respectively were prepared by standard solid state reaction method. For the first series of this study, Eu(Ba1-xPrxhCu307_0 rods were prepared to investigate the influences of changes in structure and the expected decrease in average Cu valence on oxygen sensing properties. X-ray powder diffraction analysis showed that orthorhombicity of the structure reduces with increasing Pr concentration. After the hot-spot became visible, samples x=O and x=0.05 showed a sudden drop in current before remaining constant with increasing voltage. This is suggested to be due to steep increase in resistivity caused by the sudden increase in temperature of the hot-spot together with the structural changes that lead to reduction in oxygen content. However, for the x=0.25 and x=0.4 rods the output current shows no sudden drop. The results also showed that the reduced magnitude of the output current with increasing Pr could be attributed to the reduction in intrinsic hole concentration. The output current for all samples showed strong dependence on p02. Although the sensitivity of the output current to p02 between 50% p02 and 100% p02 reduces with increasing x, the stability and repeatability of the output current seems to improve. Also, while Pr doped Eu(BaixPrx) 2Cu307_0 reduces the magnitude of the output current, it produces better response time towards different p02. On the other hand, Eui-yPryBazCu307-a rods were prepared and X-Ray powder diffraction analysis showed that, Pr doped Eu1-yPryBazCu307-o were all orthorhombic in unit cell structure with reduction in orthorhombicity upon doping. The /-V curve showed a relatively constant output current after the appearance of hot-spot. Meanwhile, the magnitude of the constant output current was observed to be decreasing with increasing Pr doping which indicates possible reduction in intrinsic hole concentration. In addition, the output current for rods with y=O.O, 0.05 and 0.10 showed a sudden drop upon the appearance of hot-spot, due to the sudden increase in hot-spot temperature, before becoming slightly constant. However, the sudden drop of output current upon appearance of hot-spot was not observed when Pr was increased to y=0.15 and 0.20 but instead a stable output current was observed. Interestingly, the output current after appearance of hot-spot for all rods showed strong dependency on ambient oxygen concentration. The sensitivity for each rod however, reduces with increasing ambient oxygen concentration. Pr doped Eui-yPryBazCu307_0 seems to prevent the sensitivity from dropping to almost zero as was the case of Eu(Ba1_ yPry)2Cu30 7_0 rods due to existence of Cu-0 chains in the orthorhombic structure. Pr doping (for y=O.lO) has also resulted in better oxygen absorption response time and better output current stability compared to other rods.
format	Thesis
qualification_name	Master of Philosophy (M.Phil.)
qualification_level	Master's degree
author	Adzam, Mohd Ikhwan
author_facet	Adzam, Mohd Ikhwan
author_sort	Adzam, Mohd Ikhwan
title	Oxygen sensing behaviors of Eu (Ba1-xPrx)2Cu3O7-δ and Eu1-yPrBa2Cu3O7-δ ceramic rods with hot-spot / Ikhwan Adzam
title_short	Oxygen sensing behaviors of Eu (Ba1-xPrx)2Cu3O7-δ and Eu1-yPrBa2Cu3O7-δ ceramic rods with hot-spot / Ikhwan Adzam
title_full	Oxygen sensing behaviors of Eu (Ba1-xPrx)2Cu3O7-δ and Eu1-yPrBa2Cu3O7-δ ceramic rods with hot-spot / Ikhwan Adzam
title_fullStr	Oxygen sensing behaviors of Eu (Ba1-xPrx)2Cu3O7-δ and Eu1-yPrBa2Cu3O7-δ ceramic rods with hot-spot / Ikhwan Adzam
title_full_unstemmed	Oxygen sensing behaviors of Eu (Ba1-xPrx)2Cu3O7-δ and Eu1-yPrBa2Cu3O7-δ ceramic rods with hot-spot / Ikhwan Adzam
title_sort	oxygen sensing behaviors of eu (ba1-xprx)2cu3o7-δ and eu1-yprba2cu3o7-δ ceramic rods with hot-spot / ikhwan adzam
granting_institution	Universiti Teknologi MARA
granting_department	Faculty of Applied Sciences
publishDate	2015
url	https://ir.uitm.edu.my/id/eprint/14044/1/TM_MOHD%20IKHWAN%20ADZAM%20AS%2015_5.pdf
_version_	1783733202144198656

Oxygen sensing behaviors of Eu (Ba1-xPrx)2Cu3O7-δ and Eu1-yPrBa2Cu3O7-δ ceramic rods with hot-spot / Ikhwan Adzam

Similar Items