Rheological and mechanical properties of Yttria Stabilized Zirconia (YSZ) produced by ceramic injection moulding / Mahfuzah Zainudin

Powder Injection Moulding (PIM) is a promising approach to producing a near netshape product of intricate geometry with cost-effective production. PIM by using ceramic powders has been studied recently due to interest as ceramic biomaterials. Yttria Stabilized Zirconia (YSZ) powders are renowned mat...

Full description

Saved in:
Bibliographic Details
Main Author: Zainudin, Mahfuzah
Format: Thesis
Language:English
Published: 2017
Subjects:
Online Access:https://ir.uitm.edu.my/id/eprint/18843/1/18843.PDF
Tags: Add Tag
No Tags, Be the first to tag this record!
id my-uitm-ir.18843
record_format uketd_dc
spelling my-uitm-ir.188432024-08-02T02:53:12Z Rheological and mechanical properties of Yttria Stabilized Zirconia (YSZ) produced by ceramic injection moulding / Mahfuzah Zainudin 2017 Zainudin, Mahfuzah Mechanics applied to machinery. Dynamics Powder Injection Moulding (PIM) is a promising approach to producing a near netshape product of intricate geometry with cost-effective production. PIM by using ceramic powders has been studied recently due to interest as ceramic biomaterials. Yttria Stabilized Zirconia (YSZ) powders are renowned materials with their, biocompatibility, superior dimensional stability and excellent mechanical properties resulting from mechanisms of transformation toughening. The focus of this study is to fabricate root pins for dental implantation structure through Ceramic Injection Moulding (CIM). 3 mol% YSZ powders were used to mix with binder components that consist of palm stearin (PS) as a primary binder and polyethylene (PE) as a backbone binder in 60:40 ratios. Four different powder loadings were prepared in this study; 57, 58, 59 and 60 vol. % based on critical powder volume percentage (CPVP) experiment. The homogeneity of the feedstocks was evaluated via torque rheometry data and scanning electron microscopy (SEM) observation. The flow ability of the feedstock were determined through rheological characteristic which are the relationship of viscosity and shear rate formed pseudoplastic behaviour, the flow behaviour index value (n) is below than 1 and lower activation energy (E). Then, all feedstocks were injected in a screw thread shape and rectangular bar mould for further experiment. All moulded specimens were embedded into alumina powder (wicking agent) before undergoing thermal debinding process at 550°C to remove the binders and pre-sintering at 1100°C was carried out simultaneously after debinding process in the same furnace. The parts were subsequently sintered in the furnace up to 1450°C for 3 hours without wicking agent with 3°C/min heating rate. The characterization of sintered parts, physical properties, and mechanical properties was performed. It is expected that, low powder loading specimens (57 vol. %) had lower viscosity, strength, density and hardness but higher in porosity compared to higher powder loading specimens (58 vol. %, 59 vol. % and 60 vol. %). The elastic modulus of compressive strength and hardness for 60 vol. % specimens was 4.79 ± 1.24 GPa and 398.5±10.4 HV respectively. Overall, root pins for dental implantation structure was successfully fabricated via CIM technique using PS as the binder system. 2017 Thesis https://ir.uitm.edu.my/id/eprint/18843/ https://ir.uitm.edu.my/id/eprint/18843/1/18843.PDF text en public mphil masters Universiti Teknologi MARA Faculty of Mechanical Engineering
institution Universiti Teknologi MARA
collection UiTM Institutional Repository
language English
topic Mechanics applied to machinery
Dynamics
spellingShingle Mechanics applied to machinery
Dynamics
Zainudin, Mahfuzah
Rheological and mechanical properties of Yttria Stabilized Zirconia (YSZ) produced by ceramic injection moulding / Mahfuzah Zainudin
description Powder Injection Moulding (PIM) is a promising approach to producing a near netshape product of intricate geometry with cost-effective production. PIM by using ceramic powders has been studied recently due to interest as ceramic biomaterials. Yttria Stabilized Zirconia (YSZ) powders are renowned materials with their, biocompatibility, superior dimensional stability and excellent mechanical properties resulting from mechanisms of transformation toughening. The focus of this study is to fabricate root pins for dental implantation structure through Ceramic Injection Moulding (CIM). 3 mol% YSZ powders were used to mix with binder components that consist of palm stearin (PS) as a primary binder and polyethylene (PE) as a backbone binder in 60:40 ratios. Four different powder loadings were prepared in this study; 57, 58, 59 and 60 vol. % based on critical powder volume percentage (CPVP) experiment. The homogeneity of the feedstocks was evaluated via torque rheometry data and scanning electron microscopy (SEM) observation. The flow ability of the feedstock were determined through rheological characteristic which are the relationship of viscosity and shear rate formed pseudoplastic behaviour, the flow behaviour index value (n) is below than 1 and lower activation energy (E). Then, all feedstocks were injected in a screw thread shape and rectangular bar mould for further experiment. All moulded specimens were embedded into alumina powder (wicking agent) before undergoing thermal debinding process at 550°C to remove the binders and pre-sintering at 1100°C was carried out simultaneously after debinding process in the same furnace. The parts were subsequently sintered in the furnace up to 1450°C for 3 hours without wicking agent with 3°C/min heating rate. The characterization of sintered parts, physical properties, and mechanical properties was performed. It is expected that, low powder loading specimens (57 vol. %) had lower viscosity, strength, density and hardness but higher in porosity compared to higher powder loading specimens (58 vol. %, 59 vol. % and 60 vol. %). The elastic modulus of compressive strength and hardness for 60 vol. % specimens was 4.79 ± 1.24 GPa and 398.5±10.4 HV respectively. Overall, root pins for dental implantation structure was successfully fabricated via CIM technique using PS as the binder system.
format Thesis
qualification_name Master of Philosophy (M.Phil.)
qualification_level Master's degree
author Zainudin, Mahfuzah
author_facet Zainudin, Mahfuzah
author_sort Zainudin, Mahfuzah
title Rheological and mechanical properties of Yttria Stabilized Zirconia (YSZ) produced by ceramic injection moulding / Mahfuzah Zainudin
title_short Rheological and mechanical properties of Yttria Stabilized Zirconia (YSZ) produced by ceramic injection moulding / Mahfuzah Zainudin
title_full Rheological and mechanical properties of Yttria Stabilized Zirconia (YSZ) produced by ceramic injection moulding / Mahfuzah Zainudin
title_fullStr Rheological and mechanical properties of Yttria Stabilized Zirconia (YSZ) produced by ceramic injection moulding / Mahfuzah Zainudin
title_full_unstemmed Rheological and mechanical properties of Yttria Stabilized Zirconia (YSZ) produced by ceramic injection moulding / Mahfuzah Zainudin
title_sort rheological and mechanical properties of yttria stabilized zirconia (ysz) produced by ceramic injection moulding / mahfuzah zainudin
granting_institution Universiti Teknologi MARA
granting_department Faculty of Mechanical Engineering
publishDate 2017
url https://ir.uitm.edu.my/id/eprint/18843/1/18843.PDF
_version_ 1811768599773184000