Influence of divalent sr²ᶧ, zn²ᶧ and ca²ᶧ substitutions on ultrasonic velocity and elastic properties of dyba₂cu₃o₇₋ᵟ high temperature superconductors / Norashikin Abdul Rasih
Ultrasonic longitudinal velocity measurements between 80 K and 280 K and shear velocity measurements between 80 K and 220 K have been performed in polycrystalline superconducting DyBa2-jSrjCu307.s (x = 0, 0.3, 0.6), DyBa2Cu3_ xZn^07.j (x - 0.01 and 0.03) and Dyo.9Cao.1Ba2Cu3-jZnjO7.tf (x = 0.01) sam...
Saved in:
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English |
| Published: |
2011
|
| Subjects: | |
| Online Access: | https://ir.uitm.edu.my/id/eprint/39754/1/39754.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Ultrasonic longitudinal velocity measurements between 80 K and 280 K and shear velocity measurements between 80 K and 220 K have been performed in polycrystalline superconducting DyBa2-jSrjCu307.s (x = 0, 0.3, 0.6), DyBa2Cu3_ xZn^07.j (x - 0.01 and 0.03) and Dyo.9Cao.1Ba2Cu3-jZnjO7.tf (x = 0.01) samples utilizing the pulsed-echo-overlap technique. A step-like longitudinal anomaly characterized by a step-like slope change was observed at 240 K for x = 0 and x = 0.3 and at 260 K for x = 0.6 in DyBa2-jSrjCu307.s samples. In addition, a longitudinal anomaly was also observed at around 240 K for DyBa2Cu3.jZni.x07.5 (x = 0) and at 230 K for x = 0.01 and 0.03. Substitution of Zn2+ which caused suppression of critical temperature, Tc however, did not suppress the step-like anomaly. On the other hand, substitution of Ca in Dyo.9Cao.iBa2Cu3.>,Zni.707.j (y = 0.01) caused the step-like anomaly to disappear. The step-like anomalies observed in samples were suggested due to oxygen ordering process in Cu-0 chains during a phase transition process at low temperatures. For DyBa2.jSrjCu3O7.tf (x = 0, 0.3, 0.6), the reduction in the slope change of the step-like anomalies indicates some degree of weakening of oxygen ordering due to the Sr substitution. Substitution of Zn2+ ions in place of Cu in Dyo.9Cao.1Ba2Cu3-jZnjO7.tf (x = 0.01 and x = 0.03) was suggested to go into Cu-0 planes and did not interfere with oxygen ordering in Cu-0 chains and cause nonsuppressed step-like anomalies in DyBa2Cu3.jZni.j07.§ (x = 0.01 and 0.03) samples. But, disappearance of the step-like anomaly due to Ca2+ substitution in Dyo.9Cao.1Ba2Cu3.jZnjO7.tf (x = 0.01) is probably related to reduction in oxygen content which depletes at Cu-0 chain sites. On the other hand, it was found that Sr substitution in DyBa2-jSrjCu307.g (x = 0, 0.3 and 0.6), Zn substitution in DyBa2Cu3_ jZn1.jO7.tf (x = 0.01 and 0.03) and Ca substitution in Dyo.9Cao.iBa2Cu3.>Zni-) ,07-tf (v = 0.01) has the effect of lowering the calculated Debye temperature and BCS electron-phonon coupling constant, signifying that the step-like anomaly may not be related to superconductivity. A comparison between experimental data and calculated lattice anharmonicity curve based on the model by Lakkad (1971) showed that the large deviation of the experimental velocity curves for DyBa2.jSrjCu3O7.tf (x = 0, 0.3) and DyBa2Cu3.jZn1.jO7.tf (x = 0, 0.01 and 0.03) from the calculated curves is strongly influenced by the existence of the step-like longitudinal anomalies. |
|---|