Application of chitosan biopolymer as a sensing material
The chitosan solution has been succesfully deposited on the silicon wafer using sol-gel method to fabricate the chitosan thin film sensors. The effect of different annealing temperature and annealing time to their electrical characteristics were studied without and under light illumination. The curr...
Saved in:
| 主要作者: | |
|---|---|
| 格式: | Thesis |
| 語言: | English |
| 主題: | |
| 在線閱讀: | http://dspace.unimap.edu.my:80/xmlui/bitstream/123456789/12849/1/p.%201-24.pdf http://dspace.unimap.edu.my:80/xmlui/bitstream/123456789/12849/2/Full%20Text.pdf |
| 標簽: |
添加標簽
沒有標簽, 成為第一個標記此記錄!
|
| 總結: | The chitosan solution has been succesfully deposited on the silicon wafer using sol-gel method to fabricate the chitosan thin film sensors. The effect of different annealing temperature and annealing time to their electrical characteristics were studied without and under light illumination. The current-voltage (I-V) characteristics showed that sensitivity of chitosan thin film sensors depend on the annealing temperature and annealing time. For the annealing temperature effect, it was found that the film annealed at 190oC has the highest photocurrent compared to the others. While for the annealing time effect, it was shown that the higher annealing time, the higher photocurrent. The changes of photocurrent are related to the different microstructure of chitosan thin film sensors. Although, the photocurrent values of the films illuminated with light exhibit the fluctuation to the photocurrent values without light illumination. Overall the chitosan thin films are sensitive to the visible and UV light. Therefore, they have a good potential as thin film light sensors. |
|---|