The effect of layer number on mechanical properties and dimensional stability of hybrid kenaf-glass fiber unsaturated polyester composite
Hybrid kenaf-glass fiber unsaturated polyester composite was prepared by hand lay-up technique. The kenaf was used in a fiber mat form. The effect of layer number of hybrid kenaf-glass fiber unsaturated polyester composite on mechanical properties and dimensional stability were studied. The effec...
Saved in:
| 主要作者: | |
|---|---|
| 格式: | Thesis |
| 语言: | English |
| 主题: | |
| 在线阅读: | http://dspace.unimap.edu.my:80/xmlui/bitstream/123456789/41299/1/Page%201-24.pdf http://dspace.unimap.edu.my:80/xmlui/bitstream/123456789/41299/2/Full%20text.pdf |
| 标签: |
添加标签
没有标签, 成为第一个标记此记录!
|
| 总结: | Hybrid kenaf-glass fiber unsaturated polyester composite was prepared by hand
lay-up technique. The kenaf was used in a fiber mat form. The effect of layer number of
hybrid kenaf-glass fiber unsaturated polyester composite on mechanical properties and
dimensional stability were studied. The effect of layer number of hybrid kenaf-glass
fiber unsaturated polyester composite has shown good interfacial adhesion between
matrix and fiber reinforced composite thus, increasing the tensile and flexural strength of
hybrid kenaf-glass fiber unsaturated polyester composite. Results show that four layer of
hybrid kenaf-glass fiber unsaturated polyester composite laminates have the highest
tensile strength i.e. 52.665 MPa while highest flexural strength was obtained in two layer
of hybrid kenaf-glass fiber unsaturated polyester composite laminate i.e. 92.77 MPa.
Three layer of hybrid kenaf-glass fiber unsaturated polyester composite laminate have
showed the highest thermal stability at high temperature 452.34˚C with ratio glass fiber
to kenaf 2:1. Highest dimensional stability in ethanol solution for 1800 minutes with
average of 2 % changes was shown in two layer of hybrid kenaf-glass fiber polyester
composite laminate. |
|---|