Hydrogen sensors using tapered optical fiber coated with metal oxide nanostructures synthesized via chemical bath deposition technique
In this thesis, novel optical hydrogen (H2) sensors based on manganese dioxide (MnO2), zinc oxide (ZnO) and molybdenum trioxide (MoO3) nanostructures coated on tapered multimode fiber (MMF) via chemical bath deposition (CBD) were developed and investigated. The use of H2 as a clean fuel in v...
Saved in:
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English |
| Published: |
2018
|
| Subjects: | |
| Online Access: | http://psasir.upm.edu.my/id/eprint/71435/1/FK%202018%2098%20-%20IR.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | In this thesis, novel optical hydrogen (H2) sensors based on manganese
dioxide (MnO2), zinc oxide (ZnO) and molybdenum trioxide (MoO3)
nanostructures coated on tapered multimode fiber (MMF) via chemical bath
deposition (CBD) were developed and investigated. The use of H2 as a clean
fuel in various application requires practical and robust sensors as to
minimize the risk of explosions associated with its volatile properties.
Semiconducting metal oxides (SMO) has been widely used for decades in H2
sensing purpose due to its simplicity in fabrication, low cost and high
sensitivity. Nanostructures SMO thin films as sensing layer has been
reported to enhance the sensitivity of the sensors due to its high surface
area to increase the gas molecules-sensing layer interaction. Typical SMO
gas sensors are electrical based in which conductivity changes as it reacts to
H2 gas. However, it has certain limitations such as easily affected by
electromagnetic interference (EMI) thus compromise the signal response and
small sparks could ignite massive explosion if the H2 concentration leaks is
more than 4% in the environment. On the other hand, optical sensor which
has yet well explored, offers advantages in term of size, light weight,
resistant to EMI and resilient in high temperature environment. By integrating
the optical transducer with SMO material, it can be employed as a hydrogen
gas sensor. There are various methods of producing SMO material such as
chemical and physical vapor deposition, RF sputtering, electrochemical
deposition and thermal evaporation. These techniques require complicated
setup with high operating temperature along with carrier gas during the
process and need conductive substrate to perform the procedure. These
techniques were also difficult to be implemented on optical fiber.
Alternatively, chemical bath deposition method provides simple and easy setup, low operating temperature, low cost and environmental friendly.
Therefore the author opted this method to fabricate H2 sensor using tapered
optical fiber coated with selected SMO incorporated with palladium (Pd) as a
catalyst to enhance the optical responses.
In this study, the fabricated sensor is comprised of tapered multimode silica
fiber (MMF) as the transducing platform. The tapering process is essential as
to enhance the sensitivity to the environment through the interaction of
evanescent field on the tapered surface area. The tapered region is then
coated with sensing layer which is also important factors that influence the
performance of the sensor. For this work, the author focused on a few kinds
of SMO material well-known for their electrochromic properties which are
manganese dioxide (MnO2), zinc oxide (ZnO) and molybdenum trioxide
(MoO3), combined with Pd as the catalytic layer. The SMOs were grown via
chemical bath technique and in-situ deposited onto the tapered optical fiber.
The morphology of MnO2, ZnO and MoO3 synthesized and deposited on
optical fiber were found to be nanograins, nanoflowers and nanogranules
which were well distributed over the cylindrical shaped of the tapered optical
fiber. The absorbance response of these sensors was characterized in terms
of response and recovery times, sensitivity, repeatability and selectivity. It
was discovered that the optimum thickness where the sensors of MnO2, ZnO
and MoO3 exhibited maximum absorbance response are 300 nm, 280 nm
and 250 nm respectively. It was revealed that the annealed sensor
demonstrated higher sensitivity compared to as-prepared sensor. It was
discovered that annealed Pd/MoO3 coated on tapered optical fiber sensor
exhibited highest absorbance increase of 3.80 when exposed to 1% H2 at
low operating temperature of 150oC as compared to other metal oxides
nanostructures. The response and recovery times recorded were 1.2 min
and 3.0 min. The developed MnO2, ZnO and MoO3 nanostructures coated on
tapered optical fiber sensor for H2 using CBD technique are the first of its
kind according to the author’s knowledge. |
|---|