Synthesis And Characterization Of Low Bandgap Nanocrystalline T-Zirconia
Serbuk nanohablur t-ZrO2 disintesis melalui kaedah kimia untuk mencari kemungkinan jika dop elektronik akan meningkatkan konduktiviti elektronik oksida. Y3+ ditambah sebagai penstabil untuk mengekalkan fasa t-ZrO2 manakala Nb5+ dimasukkan untuk dop elektronik. Nanocrystal t-ZrO2 powders were s...
Saved in:
Main Author: | |
---|---|
Format: | Thesis |
Language: | English |
Published: |
2007
|
Subjects: | |
Online Access: | http://eprints.usm.my/29357/1/Synthesis_and_characterization_of_low_bandgap_nanocrystalline_t-zirconia.pdf |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
id |
my-usm-ep.29357 |
---|---|
record_format |
uketd_dc |
spelling |
my-usm-ep.293572017-03-22T02:23:49Z Synthesis And Characterization Of Low Bandgap Nanocrystalline T-Zirconia 2007-07 Prastomo, Niki Q Science Serbuk nanohablur t-ZrO2 disintesis melalui kaedah kimia untuk mencari kemungkinan jika dop elektronik akan meningkatkan konduktiviti elektronik oksida. Y3+ ditambah sebagai penstabil untuk mengekalkan fasa t-ZrO2 manakala Nb5+ dimasukkan untuk dop elektronik. Nanocrystal t-ZrO2 powders were synthesized through a chemical route to seek a possibility if electronic doping would improve the electronics conductivity of the oxide. Y3+ was added as a stabilizer to retain tetragonal phase ZrO2 whereas Nb5+ was added for electronics doping. 2007-07 Thesis http://eprints.usm.my/29357/ http://eprints.usm.my/29357/1/Synthesis_and_characterization_of_low_bandgap_nanocrystalline_t-zirconia.pdf application/pdf en public masters USM Pusat Pengajian Sains Fizik |
institution |
Universiti Sains Malaysia |
collection |
USM Institutional Repository |
language |
English |
topic |
Q Science |
spellingShingle |
Q Science Prastomo, Niki Synthesis And Characterization Of Low Bandgap Nanocrystalline T-Zirconia |
description |
Serbuk nanohablur t-ZrO2 disintesis melalui kaedah kimia untuk mencari
kemungkinan jika dop elektronik akan meningkatkan konduktiviti elektronik oksida. Y3+
ditambah sebagai penstabil untuk mengekalkan fasa t-ZrO2 manakala Nb5+
dimasukkan untuk dop elektronik.
Nanocrystal t-ZrO2 powders were synthesized through a chemical route to seek
a possibility if electronic doping would improve the electronics conductivity of the oxide.
Y3+ was added as a stabilizer to retain tetragonal phase ZrO2 whereas Nb5+ was added
for electronics doping. |
format |
Thesis |
qualification_level |
Master's degree |
author |
Prastomo, Niki |
author_facet |
Prastomo, Niki |
author_sort |
Prastomo, Niki |
title |
Synthesis And Characterization
Of Low Bandgap Nanocrystalline
T-Zirconia |
title_short |
Synthesis And Characterization
Of Low Bandgap Nanocrystalline
T-Zirconia |
title_full |
Synthesis And Characterization
Of Low Bandgap Nanocrystalline
T-Zirconia |
title_fullStr |
Synthesis And Characterization
Of Low Bandgap Nanocrystalline
T-Zirconia |
title_full_unstemmed |
Synthesis And Characterization
Of Low Bandgap Nanocrystalline
T-Zirconia |
title_sort |
synthesis and characterization
of low bandgap nanocrystalline
t-zirconia |
granting_institution |
USM |
granting_department |
Pusat Pengajian Sains Fizik |
publishDate |
2007 |
url |
http://eprints.usm.my/29357/1/Synthesis_and_characterization_of_low_bandgap_nanocrystalline_t-zirconia.pdf |
_version_ |
1747820132199038976 |