Microstructure And Compressive Properties Of Aluminum Foam Fabricated Using Sintering Dissolution Process
Sintering dissolution process (SDP) is a technique which enables fabrication of aluminum foam as a suitable absorber material with good quality. The aim of this research is to study the effect of various parameters towards morphology and compression properties of aluminum foam fabricated using SD...
Saved in:
Main Author: | |
---|---|
Format: | Thesis |
Language: | English |
Published: |
2011
|
Subjects: | |
Online Access: | http://eprints.usm.my/45841/1/Nur%20Surianni%20Ahamad%20Suffin24.pdf |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
id |
my-usm-ep.45841 |
---|---|
record_format |
uketd_dc |
spelling |
my-usm-ep.458412019-12-12T06:14:27Z Microstructure And Compressive Properties Of Aluminum Foam Fabricated Using Sintering Dissolution Process 2011-07 Suffin, Nur Surianni Ahamad TN1-997 Mining engineering. Metallurgy Sintering dissolution process (SDP) is a technique which enables fabrication of aluminum foam as a suitable absorber material with good quality. The aim of this research is to study the effect of various parameters towards morphology and compression properties of aluminum foam fabricated using SDP method. In this research, sodium chloride (NaCl) powders were used as space holder. Aluminum foams were fabricated using SDP method which involves milling (1 hour), compaction (200 MPa), sintering (570 ºC) and dissolution process (90 ºC). The first part of this research is to investigate the effect of different space holder content in aluminum foam on density, morphology, compression properties and energy absorption. The result shows that the space holder contributes to higher porosity and energy absorption which prevented the foam structure from collapsed during compression loading. In contrast, too high space holder content leading to high tendency of residual NaCl particles in aluminum foam which resulted in porous foam with lower compression properties and energy absorption. It was found that increasing dissolution time improved energy absorption due to complete dissolution of NaCl particles. 2011-07 Thesis http://eprints.usm.my/45841/ http://eprints.usm.my/45841/1/Nur%20Surianni%20Ahamad%20Suffin24.pdf application/pdf en public masters Universiti Sains Malaysia Pusat Pengajian Kejuruteraan Bahan & Sumber Mineral |
institution |
Universiti Sains Malaysia |
collection |
USM Institutional Repository |
language |
English |
topic |
TN1-997 Mining engineering Metallurgy |
spellingShingle |
TN1-997 Mining engineering Metallurgy Suffin, Nur Surianni Ahamad Microstructure And Compressive Properties Of Aluminum Foam Fabricated Using Sintering Dissolution Process |
description |
Sintering dissolution process (SDP) is a technique which enables fabrication of
aluminum foam as a suitable absorber material with good quality. The aim of this
research is to study the effect of various parameters towards morphology and
compression properties of aluminum foam fabricated using SDP method. In this
research, sodium chloride (NaCl) powders were used as space holder. Aluminum
foams were fabricated using SDP method which involves milling (1 hour),
compaction (200 MPa), sintering (570 ºC) and dissolution process (90 ºC). The first
part of this research is to investigate the effect of different space holder content in
aluminum foam on density, morphology, compression properties and energy
absorption. The result shows that the space holder contributes to higher porosity and
energy absorption which prevented the foam structure from collapsed during
compression loading. In contrast, too high space holder content leading to high
tendency of residual NaCl particles in aluminum foam which resulted in porous foam
with lower compression properties and energy absorption. It was found that
increasing dissolution time improved energy absorption due to complete dissolution
of NaCl particles. |
format |
Thesis |
qualification_level |
Master's degree |
author |
Suffin, Nur Surianni Ahamad |
author_facet |
Suffin, Nur Surianni Ahamad |
author_sort |
Suffin, Nur Surianni Ahamad |
title |
Microstructure And Compressive Properties Of
Aluminum Foam Fabricated Using
Sintering Dissolution Process |
title_short |
Microstructure And Compressive Properties Of
Aluminum Foam Fabricated Using
Sintering Dissolution Process |
title_full |
Microstructure And Compressive Properties Of
Aluminum Foam Fabricated Using
Sintering Dissolution Process |
title_fullStr |
Microstructure And Compressive Properties Of
Aluminum Foam Fabricated Using
Sintering Dissolution Process |
title_full_unstemmed |
Microstructure And Compressive Properties Of
Aluminum Foam Fabricated Using
Sintering Dissolution Process |
title_sort |
microstructure and compressive properties of
aluminum foam fabricated using
sintering dissolution process |
granting_institution |
Universiti Sains Malaysia |
granting_department |
Pusat Pengajian Kejuruteraan Bahan & Sumber Mineral |
publishDate |
2011 |
url |
http://eprints.usm.my/45841/1/Nur%20Surianni%20Ahamad%20Suffin24.pdf |
_version_ |
1747821578594287616 |