Corrosion assessment on reinforced concrete and its service life prediction
Deterioration of structural concrete may be caused either by chemical or physical effects. Corrosion of embedded steel is a major cause of deterioration of concrete structures at the present time. This lead to structural weakening due to loss of steel cross-section, surface staining, cracking or spa...
Saved in:
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English |
| Published: |
2005
|
| Subjects: | |
| Online Access: | http://eprints.uthm.edu.my/3265/1/SYED%20BURHANUDDIN%20HILMI%20SYED%20MOHAMAD%20-%2024p.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| id |
my-uthm-ep.3265 |
|---|---|
| record_format |
uketd_dc |
| spelling |
my-uthm-ep.32652022-02-03T01:53:11Z Corrosion assessment on reinforced concrete and its service life prediction 2005 Syed Mohamad, Syed Burhanuddin Hilmi TA401-492 Materials of engineering and construction. Mechanics of materials Deterioration of structural concrete may be caused either by chemical or physical effects. Corrosion of embedded steel is a major cause of deterioration of concrete structures at the present time. This lead to structural weakening due to loss of steel cross-section, surface staining, cracking or spalling and delamination of concrete and then gradually reduces the service life of the reinforced concrete structures. The most biggest problem is concerned with the structural integrity and safety of reinforced concrete structures by reducing the load carrying capacity. This project was to assess the degree of corrosion on reinforced concrete structure and estimating the residual service life. It was conducted based on electrochemical methods. These methods include galvanostatic pulse method and linear polarization method. A Non-Destructive Test techniques called GalvaPulse was used in this study. These equipments allow us to determine the degree of corrosion, rate of corrosion and interpret the result in corrosion mapping. From the results, assessment on the validation of corrosion in short and long terms by using predictive models are discussed. 2005 Thesis http://eprints.uthm.edu.my/3265/ http://eprints.uthm.edu.my/3265/1/SYED%20BURHANUDDIN%20HILMI%20SYED%20MOHAMAD%20-%2024p.pdf text en public mphil masters Universiti Tun Hussein Onn Malaysia Faculty of Civil Engineering |
| institution |
Universiti Tun Hussein Onn Malaysia |
| collection |
UTHM Institutional Repository |
| language |
English |
| topic |
TA401-492 Materials of engineering and construction Mechanics of materials |
| spellingShingle |
TA401-492 Materials of engineering and construction Mechanics of materials Syed Mohamad, Syed Burhanuddin Hilmi Corrosion assessment on reinforced concrete and its service life prediction |
| description |
Deterioration of structural concrete may be caused either by chemical or physical effects. Corrosion of embedded steel is a major cause of deterioration of concrete structures at the present time. This lead to structural weakening due to loss of steel cross-section, surface staining, cracking or spalling and delamination of concrete and then gradually reduces the service life of the reinforced concrete structures. The most biggest problem is concerned with the structural integrity and safety of reinforced concrete structures by reducing the load carrying capacity. This project was to assess the degree of corrosion on reinforced concrete structure and estimating the residual service life. It was conducted based on electrochemical methods. These methods include galvanostatic pulse method and linear polarization method. A Non-Destructive Test techniques called GalvaPulse was used in this study. These equipments allow us to determine the degree of corrosion, rate of corrosion and interpret the result in corrosion mapping. From the results, assessment on the validation of corrosion in short and long terms by using predictive models are discussed. |
| format |
Thesis |
| qualification_name |
Master of Philosophy (M.Phil.) |
| qualification_level |
Master's degree |
| author |
Syed Mohamad, Syed Burhanuddin Hilmi |
| author_facet |
Syed Mohamad, Syed Burhanuddin Hilmi |
| author_sort |
Syed Mohamad, Syed Burhanuddin Hilmi |
| title |
Corrosion assessment on reinforced concrete and its service life prediction |
| title_short |
Corrosion assessment on reinforced concrete and its service life prediction |
| title_full |
Corrosion assessment on reinforced concrete and its service life prediction |
| title_fullStr |
Corrosion assessment on reinforced concrete and its service life prediction |
| title_full_unstemmed |
Corrosion assessment on reinforced concrete and its service life prediction |
| title_sort |
corrosion assessment on reinforced concrete and its service life prediction |
| granting_institution |
Universiti Tun Hussein Onn Malaysia |
| granting_department |
Faculty of Civil Engineering |
| publishDate |
2005 |
| url |
http://eprints.uthm.edu.my/3265/1/SYED%20BURHANUDDIN%20HILMI%20SYED%20MOHAMAD%20-%2024p.pdf |
| _version_ |
1747831030669115392 |