Investigation into some aspects of partial ductile mode in wet andd dry grinding of optical glass

Machining of hard and brittle materials always pose problems such as rough surface, cracks, subsurface damage and residual stresses mainly due to its brittle nature. Recent developments in cutting tool technology coupled with rigid ultraprecision machine tools have made it possible to machine hard a...

Full description

Saved in:

Bibliographic Details
Main Author:	Sudin, I.
Format:	Thesis
Published:	2004
Subjects:	TJ Mechanical engineering and machinery
Tags:	Add Tag No Tags, Be the first to tag this record!

id	my-utm-ep.6869
record_format	uketd_dc
spelling	my-utm-ep.68692011-01-21T05:53:17Z Investigation into some aspects of partial ductile mode in wet andd dry grinding of optical glass 2004 Sudin, I. TJ Mechanical engineering and machinery Machining of hard and brittle materials always pose problems such as rough surface, cracks, subsurface damage and residual stresses mainly due to its brittle nature. Recent developments in cutting tool technology coupled with rigid ultraprecision machine tools have made it possible to machine hard and brittle materials like optical glass in ductile mode with crack free surfaces. However this technique is reported to be relatively slow and too expensive for manufacturing less precision products like ophthalmic lenses, which do not require extreme form accuracy. Though not possible to machine glass in fully ductile mode with conventional grinding, substantial amount of partial ductile mode areas generated on the ground surface is proven to reduce polishing time significantly to get mirror finish. In this study, resinoid bonded diamond pins, with and without a central hole were used to grind BK7 optical glass. Plano grinding operation was carried out using a high-speed jig grinder air motor, which was attached to a vertical spindle CNC milling machine. Both wet and dry grinding operations were performed. In wet grinding, ductile-fracture areas and surface roughness of ground surface were investigated by varying grinding conditions. Diamond grinding pins with and without central hole were found to have an effect on surface finish and flatness on the ground surfaces. Central holed diamond pins produced better surface finish and were 5 times superior in flatness compared to surfaces ground with diamond pins without central hole. Subsequently, zero velocity effect that cause chips trapped underneath of diamond pins are completely eliminated. Insufficient coolant penetration into grinding zone and fixture rigidity were found to have contributed stalling marks. Applications of higher coolant flow rate of 5 litres/min together with a rigid pocket groove holder were successfully used to eliminate stalling and this set-up was used in subsequent experimental trials for ductile-fracture and surface roughness analysis. Maximum ductile streaks were obtained at the lowest feed (5mm/min) and in-feed (5Âµm) for both 64Âµm and 126Âµm grit diamond pins. Finer ductile streaks were observed with 64Âµm than 126Âµm grit diamond pins in almost all conditions probably due to grain size effects. An image processing procedure has been successfully developed to quantify objectively the fraction of ductile and fracture areas generated on ground surfaces. Among the four alternatives developed, method B provided the least error. A linear relationship model was established for surface roughness when grinding with 64Âµm grit diamond pins. The feed was found to have significant effect on the response investigated. The model was verified by the confirmation run and therefore can be used for prediction within the limits of the factors investigated. In dry grinding, various types of chips morphology were observed. A discovery was made during this study, namely the observation of solid spherical glass chips obtained at the lowest cutting condition (feed = 2.5mm/min and infeed = 5Âµm) and its formation mechanism is described. 2004 Thesis http://eprints.utm.my/id/eprint/6869/ http://sps.utm.my phd doctoral Universiti Teknologi Malaysia, Faculty of Mechanical Engineering Mechanical Engineering
institution	Universiti Teknologi Malaysia
collection	UTM Institutional Repository
topic	TJ Mechanical engineering and machinery
spellingShingle	TJ Mechanical engineering and machinery Sudin, I. Investigation into some aspects of partial ductile mode in wet andd dry grinding of optical glass
description	Machining of hard and brittle materials always pose problems such as rough surface, cracks, subsurface damage and residual stresses mainly due to its brittle nature. Recent developments in cutting tool technology coupled with rigid ultraprecision machine tools have made it possible to machine hard and brittle materials like optical glass in ductile mode with crack free surfaces. However this technique is reported to be relatively slow and too expensive for manufacturing less precision products like ophthalmic lenses, which do not require extreme form accuracy. Though not possible to machine glass in fully ductile mode with conventional grinding, substantial amount of partial ductile mode areas generated on the ground surface is proven to reduce polishing time significantly to get mirror finish. In this study, resinoid bonded diamond pins, with and without a central hole were used to grind BK7 optical glass. Plano grinding operation was carried out using a high-speed jig grinder air motor, which was attached to a vertical spindle CNC milling machine. Both wet and dry grinding operations were performed. In wet grinding, ductile-fracture areas and surface roughness of ground surface were investigated by varying grinding conditions. Diamond grinding pins with and without central hole were found to have an effect on surface finish and flatness on the ground surfaces. Central holed diamond pins produced better surface finish and were 5 times superior in flatness compared to surfaces ground with diamond pins without central hole. Subsequently, zero velocity effect that cause chips trapped underneath of diamond pins are completely eliminated. Insufficient coolant penetration into grinding zone and fixture rigidity were found to have contributed stalling marks. Applications of higher coolant flow rate of 5 litres/min together with a rigid pocket groove holder were successfully used to eliminate stalling and this set-up was used in subsequent experimental trials for ductile-fracture and surface roughness analysis. Maximum ductile streaks were obtained at the lowest feed (5mm/min) and in-feed (5Âµm) for both 64Âµm and 126Âµm grit diamond pins. Finer ductile streaks were observed with 64Âµm than 126Âµm grit diamond pins in almost all conditions probably due to grain size effects. An image processing procedure has been successfully developed to quantify objectively the fraction of ductile and fracture areas generated on ground surfaces. Among the four alternatives developed, method B provided the least error. A linear relationship model was established for surface roughness when grinding with 64Âµm grit diamond pins. The feed was found to have significant effect on the response investigated. The model was verified by the confirmation run and therefore can be used for prediction within the limits of the factors investigated. In dry grinding, various types of chips morphology were observed. A discovery was made during this study, namely the observation of solid spherical glass chips obtained at the lowest cutting condition (feed = 2.5mm/min and infeed = 5Âµm) and its formation mechanism is described.
format	Thesis
qualification_name	Doctor of Philosophy (PhD.)
qualification_level	Doctorate
author	Sudin, I.
author_facet	Sudin, I.
author_sort	Sudin, I.
title	Investigation into some aspects of partial ductile mode in wet andd dry grinding of optical glass
title_short	Investigation into some aspects of partial ductile mode in wet andd dry grinding of optical glass
title_full	Investigation into some aspects of partial ductile mode in wet andd dry grinding of optical glass
title_fullStr	Investigation into some aspects of partial ductile mode in wet andd dry grinding of optical glass
title_full_unstemmed	Investigation into some aspects of partial ductile mode in wet andd dry grinding of optical glass
title_sort	investigation into some aspects of partial ductile mode in wet andd dry grinding of optical glass
granting_institution	Universiti Teknologi Malaysia, Faculty of Mechanical Engineering
granting_department	Mechanical Engineering
publishDate	2004
_version_	1747814697921413120

Investigation into some aspects of partial ductile mode in wet andd dry grinding of optical glass

Similar Items